SP ® ZINS – 710 EPOXY HEAT - RESISANT RICH ZINC PRIMING PAINT

MSP:

Product Description

SP®ZINS - 710 is a two-component, self-curing, ethyl silicate zinc-plated primer. Bonded matt, flat, abrasion resistant, excellent weather resistance. Protect steel surfaces at high temperatures such as tanks, chemical compartments, chimneys... SP®ZINS - 710 is compatible with many coatings such as Epoxy, Silicone and Polyurethane.
  • High adhesion.
  • Durable with saline, petroleum, sea water, fresh water, chemicals in pH range 5-9.
  • High abrasion resistance.
  • High heat resistance. It can be used for heated surfaces up to 400 0C (discontinuous).

- For surface of new untreated steel: Grade of cleanliness is Sa 2.5 (ISO 8501-1: 1998). Mechanical cleaning up to the minimum standard of St2 (ISO 8501-1: 1998) may be acceptable depending on the intended use.

- For temporary primer-coated steel surfaces: The appropriate temporary primer coat surfaces should be  clean, dry, free from contamination and free of any foreign matter, such as oil and grease.

- For surface had old painting layer: The appropriate primer must be dry, clean and free from decomposition

  • Stir the A part by stirrer. Slowly pour part B into container has part A at a rate of 41 parts A and 59 parts

B.

  • Dry Film Thickness Reference:

Use as coating: 75 μm.

Primer for heat-resistant coatings: 30 - 50 μm.

  • Use only the recommended solvent (maximum 5% of weight of A & B mix). Mixing should not exceed 6 hours at 23 0C.
Color:

Gray Zinc

Solid content:

Min 70%

proportion:

4 - 6 m 2 / kg / 30μm (depending on surface conditions)

Theoretical coverage:

2.03 ± 0.05g/ml

Mixing ratio A/B:

41 / 59 (by volume)

Film thickness:

Wet thickness: 65µm

Dry thickness: 30µm

dried(23°C):

Touchable dry 10 minutes

Hard dry 2h

Time coating layer (23°C):

Minimum after 2h

Time live (after mixing):

6 hours

Diluent:

SPTHINNER 401