SP ® ZINP - 101 EPOXY ZINC PHOSPHATE PRIMING PAINT

MSP:

Product Description

  • High adhesion.
  • Durable with petroleum, sea water, fresh water, chemicals, climate.
  • High heat resistance. This paint can be used for heated surfaces up to 1100C.

The surface should be dry, clean, free of any other impurities. The surface should be assessed and treated

in accordance with ISO 8504.

For surface of new untreated steel: Grade of cleanliness is Sa 2.5 (ISO 8501-1: 1998). Mechanical cleaning up to the minimum standard of St2 (ISO 8501-1: 1998) may be acceptable depending on the intended use.

For temporary primer-coated steel surfaces: The appropriate temporary primer coat surfaces should be

clean, dry, free from contamination and free of any foreign matter, such as oil and grease.

For surface had old painting layer: The appropriate primer must be dry, clean and free from decomposition.

  • Stir the base part (part A) with a stirrer. Slowly pour the curing portion (part B) into the container has part
  • A at a rate of 10 parts A and 1 part B. Stir evenly for 3 minutes until the mixture is homogeneous.
  • Use only the solvent when recommended (maximum 5% of weight of A & B mix).

Mixing should not exceed 6 hours at 230C.

Color:

Red, brown

Solid content:

min 55%

proportion:

5 - 7 m2/ kg / 30μm (depending on surface conditions)

Theoretical coverage:

1.45 ± 0.05g/ml

Mixing ratio A/B:

10/1(by volume)

Film thickness:

Wet thickness: 95µm

Dry thickness: 50µm

dried(23°C):

Touchable dry  2h

Hard dry 12h

Time coating layer (23°C):

Minimum after 8h

Time live (after mixing):

6 hours

Diluent:

SPTHINER 305